1.4109 / 440A / X70CrMo15 Martensitic Stainless Steel Sheet & Coil
产品参数
- 冶炼方式: 选择
- 产品尺寸: 0.1~60.0*250mm
- 交货状态: 冷轧 、
- 表面状态: Bright 、
- 库存状态: 订货
产品详情
A 276 S44002 : A 276 (2013) 化学成分
| C | Mn | Si | P | S | Cr | Ni | Mo |
|---|---|---|---|---|---|---|---|
| 0.60 - 0.75 | ≤ 1.00 | ≤ 1.00 | ≤ 0.04 | ≤ 0.03 | 16.00 - 18.00 | ≤ - | ≤ 0.75 |
A 276 S44002 : A 276 (2013) 力学性能
| 热处理 | 最小值 | 最大值 | 近似值 | 备注 |
|---|
| 热处理 | 最小值 | 最大值 | 近似值 | 备注 |
|---|
| 热处理 | 最小值 | 最大值 | 近似值 | 备注 |
|---|
| 热处理 | 最小值 | 最大值 | 近似值 | 备注 |
|---|
| 热处理 | 最小值 | 最大值 | 近似值 | 备注 |
|---|
| 热处理 | 类型 | 最小值 | 最大值 | 近似值 | 备注 |
|---|
AISI 440A ( UNS S44002 ) stainless is a high-carbon martensitic stainless steel developed to provide
stainless properties with maximum hardness.
It is magnetic in both the annealed and hardened conditions.
Maximum hardness and corrosion resistance are available only in the hardened or hardened and stress
relieved conditions, so the alloy is not used in the annealed or annealed and tempered conditions.
Dental and surgical instruments and cutlery are frequent applications for Type 440A.
Type 440A Stainless Steel in coils and cut lengths in thicknesses 0.1mm up and widths up to and including 250mm.
440A stainless High-carbon chromium steel. Provides stainless properties with excellent hardness.
Attains a hardness of Rockwell C 56 and maximum toughness when heat-treated.
Specifications: ASTM A276, ASTM A314, ASTM A473, ASTM A580, ASTM F899, AMS 5631, QQ-S-763
Grade C Si Mn Cr Mo
440A 0.60~0.75 1.00 max 1.00 max 16.00~18.00 0.75 max
440B 0.75~0.95 1.00 max 1.00 max 16.00~18.00 0.75 max
440C 0.95~1.20 1.00 max 1.00 max 16.00~18.00 0.75 max
440A is a high carbon martensitic stainless steel, this alloy can be heat treated to extremely high hardnesses.
It has slightly less carbon than 440B and 440C giving it better machinability but less hardness.
The combination of good wear resistance and high hardness makes this alloy an excellent candidate for cutting tools and knife blades.
It also is often used for dental and surgical equipment.