A-2

A-2化学成分

C	Si	Mn	Cr	Mo	V	Ni
0.95-1.05	≤1.00	≤0.50	4.75-5.50	0.90-1.40	0.15-0.50	≤0.30

---

A-2机械性能

ADVANTAGES:
Good combination of wear resistance and toughness. Very stable in heat treatment.
Not difficult to machine or grind.
Good Hardenability.
AVAILABILITY
Readily available
MACHINABILITY
A-2 can be machined readily in the fully annealed condition. Its machinability rating is about 65% of a 1% carbon tool steel. It also has a high grindability rating.
ANNEALING
Heat slowly to 1500 to 1600°F and furnace cool, allowing the temperature to drop about 75°Fper hour to 1000°F. Then air cool. The annealed hardness is 202 to 248 Brinell.

HARDENING

A-2 should be preheated at 1200° to 1300°F then taken up to 1725° to 1750°F. When part is at temperature it should be soaked 30 minutes for the first inch of thickness and 15 minutes for each inch of thickness over one inch. If a controlled atmosphere or vacuum furnace is not available then part should be wrapped in stainless foil to prevent decarburization. When the piece is taken from the furnace the stainless foil must be removed (if applicable) and then cooled in still air. Large pieces may require forced air.

TEMPERING

As soon as pieces have been cooled to room temperature (100° to 125°F) tempering must begin. Heat slowly to the tempering temperature selected to obtain the hardness desired. Double tempering is recommended.

---

A-2产品形态

• 热轧和冷拉棒材, 圆棒, 扁钢, 六角棒, 八角棒, 空心棒
• 带钢和钢卷, 热轧带钢, 热轧钢卷, 冷轧钢带, 冷轧钢卷
• 冷轧板材, 热轧板, 冷轧薄板, 中厚板, 高强钢板
• 热轧和冷拉异型钢, 凹凸字钢, 滑轨, 滑块
• 热轧和冷拉钢丝, 扁丝, 盘条, 直条
• 自由锻和模锻, 扁钢, 模块, 环, 桶, 饼, 阶梯轴及定制化
• 热挤压和冷轧无缝管, 异型管, 方管, 毛细管
• 电渣锭

---